Fail:Cold rolling of Mg and Mg-1Al-0.1Ca.jpg
Saiz pralihat ini: 800 × 523 piksel. Leraian-leraian lain: 320 × 209 piksel | 640 × 418 piksel | 895 × 585 piksel.
Fail asli (895 × 585 piksel, saiz fail: 58 KB, jenis MIME: image/jpeg)
Ringkasan
| Keterangan | Pure polycrystalline magnesium failing in a brittle manner already at low deformations, shown here in the rolled state. Pure Mg fractured along macroscopic shear bands when cold rolled to 10% thickness reduction whereas Mg-1Al-0.1Ca could be cold rolled to 54% thickness reduction in several rolling passes of 8% thickness reduction per rolling pass; small sheet sections cut from the rolled sheet after each consecutive rolling pass are presented. Early failure of pure Mg occurs due to the restriction to mainly basal <a> dislocation slip and tensile twinning. |
| Tarikh | |
| Sumber | https://www.nature.com/articles/s41598-017-10384-0 |
| Pengarang | S. Sandlöbes et al |
| Kebenaran (Penggunaan semula fail ini) |
  Fail ini dilesenkan di bawah lesen Pengiktirafan 4.0 Antarabangsa Creative Commons.
|
Sejarah fail
Klik pada tarikh/waktu untuk melihat rupa fail tersebut pada waktu itu.
| Tarikh/Waktu | Gambar kenit | Ukuran | Pengguna | Komen | |
|---|---|---|---|---|---|
| semasa | 05:02, 10 April 2019 | | 895 × 585 (58 KB) | Materialscientist | {{Information |description=Pure polycrystalline magnesium failing in a brittle manner already at low deformations, shown here in the rolled state. Pure Mg fractured along macroscopic shear bands when cold rolled to 10% thickness reduction whereas Mg-1Al-0.1Ca could be cold rolled to 54% thickness reduction in several rolling passes of 8% thickness reduction per rolling pass; small sheet sections cut from the rolled sheet after each consecutive rolling pass are presented. Early failure of pure... |
Penggunaan fail
Tiada laman yang menggunakan fail ini.
Penggunaan fail sejagat
Fail ini digunakan oleh wiki-wiki lain yang berikut:
- Penggunaan di en.wikipedia.org